Quote:
Originally Posted by Robbie.g
thanks chaps for the replies.
Silicone is not ideal as a sealant on mechanical fittings as many brands emit acetic acid on curing (they smell vinegary). This apparently is not that good on the stainless.
I belive stayloc stipulate 3M's 101, and norseman is 'polysulfide' caulk.
Regards  |
I've read the same thing about the acid in silicone. Do you have any idea if that continues to be an issue even after the material has cured?
Another question/thought I'd like to run by you, (not to hijack the thread) is about using sealants, caulks etc. in swages.
When I first started in business years ago, I had a habit of melting beeswax into the wire above the swage fittings and letting it seal the top.
Later, I began the practice of using different products on the wire before swaging. Such as locktite or 5200.
What are your thoughts about that?